DLP Materials

ROBUST MATERIALS & STRONG, END-USE PARTS

At Huntsville, our team leverages the wide range of DLP materials to produce durable and intricately detailed end-use parts for any industry.

Smarter Production

Create high strength, flexible, and heat resistant parts for low-volume production.

Heat Resistant

LOCTITE 3D IND403

A high-modulus, durable resin for improved temperature resistance.

Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation at Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80°C

Ultracur3D RG 3280

Resin filled with ceramic for outstanding stiffness and temperature resistance.

Colors: White
Ultimate Tensile Strength: 87 MPa
Elongation at Break: 1.3%
Tensile Modulus: 10600 MPa
HDT: 284°C

Tough

LOCTITE 3D 3172

Durable, high-impact material ideal for fixtures and tooling.

Colors: Grey
Ultimate Tensile Strength: 39 MPa
Elongation at Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51°C

LOCTITE 3D 3843

Semi-flexible, high-impact resin suitable for a variety of applications.

Colors: Black, Matte Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60°C

Stratasys Dura56

Tough, impact-resistant photopolymer designed for functional, high-aesthetic, and durable applications.

Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation at Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52°C

General Purpose

Ultracur3D ST45

Urethane-based polymer designed for high-performance functional components.

Colors: Black
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63°C

Somos WeatherX 100

Environmentally durable material engineered for final-use components.

Colors: Black
Ultimate Tensile Strength: 60 ± 0.3 MPa
Elongation at Break: 26% ± 6.0
Tensile Modulus: 2128 ± 154 MPa
HDT: 67° C

Elastomers

LOCTITE 3D IND402

Elastomer with high rebound and resilience, perfect for lattice structures.

Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation at Break: 230%
Tensile Modulus: 42 MPa

Medical

LOCTITE 3D MED413

Biocompatible material suitable for a wide range of medical applications.

Colors: White
Ultimate Tensile Strength: 46 MPa
Elongation at Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68°C